LNP LUBRICOMP RCL34 is a compound based on Nylon 66 containing 20% Carbon Fiber, 15% PTFE. Added features of this grade includes: Wear Resistant, Electrically Conductive.
LNP LUBRICOMP RCL26是一種基于尼龍66的化合物，含有30%的碳纖維和10%的聚四氟乙烯。該等級的附加特性包括：耐磨、導電。
| REVISION: 14/08/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, break, 5 mm/min | 204 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2.3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 15200 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 281 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 12200 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A | |
| THERMAL | ||||
| CTE, 23°C to 60°C, flow | 9.E-06 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 7.6E-05 | 1/°C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 261 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 251 | °C | ISO 75/Af | |
| PHYSICAL | ||||
| Mold Shrinkage on Tensile Bar, flow | 0.2-0.4 | % | SABIC method | |
| Density | 1.31 | g/cm3 | ISO 1183 | |
| ELECTRICAL | ||||
| Surface Resistivity | 1.E+02-1.E+03 | Ohm | ASTM D 257 | |