15%玻璃增強(qiáng) VALOX PBT Resin K4530
發(fā)布時(shí)間：2016-04-19        瀏覽次數(shù)：462        返回列表

VALOX ? Resin K4530

SI | British | Metric | PDF Europe-Africa-Middle East: COMMERCIAL

 
15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.
 

Property
 
TYPICAL PROPERTIES (1)
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min 1050 kgf/cm2 ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min 1050 kgf/cm2 ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min 4 % ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 4 % ASTM D 638
Tensile Modulus, 5 mm/min 36200 kgf/cm2 ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span 1520 kgf/cm2 ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 47300 kgf/cm2 ASTM D 790
Tensile Stress, yield, 5 mm/min 98 MPa ISO 527
Tensile Stress, break, 5 mm/min 98 MPa ISO 527
Tensile Strain, yield, 5 mm/min 3.1 % ISO 527
Tensile Strain, break, 5 mm/min 3.1 % ISO 527
Tensile Modulus, 1 mm/min 5250 MPa ISO 527
Flexural Stress, yield, 2 mm/min 150 MPa ISO 178
Flexural Stress, break, 2 mm/min 150 MPa ISO 178
Flexural Modulus, 2 mm/min 4750 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 40 cm-kgf/cm ASTM D 4812
Izod Impact, notched, 23°C 5 cm-kgf/cm ASTM D 256
Izod Impact, unnotched 80*10*4 +23°C 30 kJ/m2 ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 7 kJ/m2 ISO 180/1A
THERMAL Value Unit Standard
HDT, 0.45 MPa, 3.2 mm, unannealed 218 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 193 °C ASTM D 648
Vicat Softening Temp, Rate B/120 205 °C ISO 306
PHYSICAL Value Unit Standard
Specific Gravity 1.41 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5) 0.7 - 0.9 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm (5) 1 - 1.2 % SABIC Method
Melt Volume Rate, MVR at 250°C/2.16 kg 17 cm3/10 min ISO 1133
AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III Value Unit Standard
Tensile Stress, brk, Type I, 5 mm/min 830 kgf/cm2 ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 2.5 % ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span 46100 kgf/cm2 ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span 9.7 % ASTM D 790
Instrumented Impact, Total Energy, 23°C 60 cm-kgf ASTM D 3763
PROPERTIES AFTER 1008 HOURS AT 125?C Value Unit Standard
Tensile Stress, brk, Type I, 5 mm/min 990 kgf/cm2 ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 4 % ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span 49100 kgf/cm2 ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span 7 % ASTM D 790
Instrumented Impact, Total Energy, 23°C 50 cm-kgf ASTM D 3763
AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV Value Unit Standard
Tensile Stress, brk, Type I, 5 mm/min 910 kgf/cm2 ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 2.3 % ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span 52000 kgf/cm2 ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span 6 % ASTM D 790
Instrumented Impact, Total Energy, 23°C 50 cm-kgf ASTM D 3763
PROPERTIES AFTER 1008 HOURS AT 155?C Value Unit Standard
Tensile Stress, brk, Type I, 5 mm/min 49070 kgf/cm2 ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min 97.2 % ASTM D 638
Flexural Modulus, 1.3 mm/min, 50 mm span 0 kgf/cm2 ASTM D 790
Flexural Strain, 1.3 mm/min, 50 mm span 3.8 % ASTM D 790
Source GMD, last updated:2013/05/13
Processing

? We cannot overemphasize -- OVERDRYING SHOULD BE AVOIDED. Use a dehumidifying desiccant bed dryer with -30°C (-20°F) dew point air (approximately 1 cfm/lb/hr air flow). Exceeding the temperature or time recommended can compromise the hydrolysis performance of the material or the drying equipment can be damaged.
Parameter
Injection Molding Value Unit
Drying Temperature 60 - 75 °C
Drying Time 4 - 6 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.05 %
Melt Temperature 250 - 265 °C
Nozzle Temperature 245 - 260 °C
Front - Zone 3 Temperature 250 - 265 °C
Middle - Zone 2 Temperature 245 - 260 °C
Rear - Zone 1 Temperature 240 - 255 °C
Mold Temperature 65 - 90 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 50 - 80 rpm
Shot to Cylinder Size 40 - 80 %
Vent Depth 0.025 - 0.038 mm
Source GMD, last updated:2013/05/13
? If material is stored in dryer for extended periods (overnight or more):
    Lower dryer temperature to room temperature.
    Recirculate cool dry air over material.
 
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
 
PLEASE CONTACT US FOR AVAILABILITY IN YOUR REGION.
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
(5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(6) Needs hard coat to consistently pass 60 sec Vertical Burn. 

Disclaimer : THE MATERIALS, PRODUCTS AND SERVICES OF SAUDI BASIC INDUSTRIES CORPORATION (SABIC) or ITS SUBSIDIARIES or AFFILIATES (?SELLER?) ARE SOLD SUBJECT TO SELLER?S STANDARD CONDITIONS OF SALE, WHICH ARE AVAILABLE UPON REQUEST. INFORMATION AND RECOMMENDATIONS CONTAINED IN THIS DOCUMENT ARE GIVEN IN GOOD FAITH. HOWEVER, SELLER MAKES NO EXPRESS or IMPLIED REPRESENTATION, WARRANTY or GUARANTEE (i) THAT ANY RESULTS DESCRIBED IN THIS DOCUMENT WILL BE OBTAINED UNDER END-USE CONDITIONS, or (ii) AS TO THE EFFECTIVENESS or SAFETY OF ANY DESIGN or APPLICATION INCORPORATING SELLER?S MATERIALS, PRODUCTS, SERVICES or RECOMMENDATIONS.  UNLESS OTHERWISE PROVIDED IN SELLER?S STANDARD CONDITIONS OF SALE, SELLER SHALL NOT BE RESPONSIBLE FOR ANY LOSS RESULTING FROM ANY USE OF ITS MATERIALS, PRODUCTS, SERVICES or RECOMMENDATIONS DESCRIBED IN THIS DOCUMENT. Each user is responsible for making its own determination as to the suitability of Seller?s materials, products, services or recommendations for the user?s particular use through appropriate end-use and other testing and analysis. Nothing in any document or oral statement shall be deemed to alter or waive any provision of Seller?s Standard Conditions of Sale or this Disclaimer, unless it is specifically agreed to in a writing signed by Seller.  Statements by Seller concerning a possible use of any material, product, service or design do not, are not intended to, and should not be construed to grant any license under any patent or other intellectual property right of Seller or as a recommendation for the use of any material, product, service or design in a manner that infringes any patent or other intellectual property right.

轉(zhuǎn)載請(qǐng)注明：轉(zhuǎn)載自環(huán)球塑化資訊網(wǎng) http://647cq.com/news/
本文鏈接：http://647cq.com/b-shabo/news269600/
免責(zé)聲明：本文"15%玻璃增強(qiáng) VALOX PBT Resin K4530"僅代表作者個(gè)人觀點(diǎn)，與環(huán)球塑化網(wǎng)無關(guān)。環(huán)球塑化網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請(qǐng)與我們聯(lián)絡(luò)。電話：400-115-2868

機(jī)械手 激光機(jī)
©2024 環(huán)球塑化網(wǎng) 版權(quán)所有   技術(shù)支持： 環(huán)球塑化網(wǎng)     訪問量：526365  管理入口

收縮

  • 電話咨詢

  • 0769-82558310
QR code
關(guān)閉
關(guān)閉
請(qǐng)輸入驗(yàn)證碼