TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
1320
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
1320
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
2
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
2
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
117200
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
2030
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
2030
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
91700
|
kgf/cm2
|
ASTM D 790
|
|
Tensile Stress, yield, 5 mm/min
|
130
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
130
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
2
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
2
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
11500
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
200
|
MPa
|
ISO 178
|
|
Flexural Stress, break, 2 mm/min
|
200
|
MPa
|
ISO 178
|
|
Flexural Strain, break, 2 mm/min
|
3
|
%
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
9600
|
MPa
|
ISO 178
|
|
Hardness, H358/30
|
115
|
MPa
|
ISO 2039-1
|
|
Hardness, Rockwell R
|
118
|
-
|
ISO 2039-2
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Charpy Impact, unnotched, 23°C
|
50
|
kJ/m2
|
ISO 179/2C
|
|
Charpy Impact, unnotched, -30°C
|
50
|
kJ/m2
|
ISO 179/2C
|
|
Izod Impact, unnotched, 23°C
|
67
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, unnotched, -30°C
|
67
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, 0°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
45
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*4 -30°C
|
45
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*4 +23°C
|
8
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 0°C
|
8
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
8
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
10
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy Impact, notched, 23°C
|
11
|
kJ/m2
|
ISO 179/2C
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
10
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy Impact, notched, -30°C
|
9
|
kJ/m2
|
ISO 179/2C
|
|
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
|
50
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
|
55
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate A/50
|
220
|
°C
|
ASTM D 1525
|
|
Vicat Softening Temp, Rate B/50
|
205
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
220
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
205
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
2.18E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
8.18E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, flow
|
1.6E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, xflow
|
1.2E-04
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 150°C, flow
|
1.4E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 150°C, xflow
|
1.3E-04
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate A/50
|
220
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/50
|
205
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
205
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
220
|
°C
|
ISO 75/Be
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
220
|
°C
|
ISO 75/Bf
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
205
|
°C
|
ISO 75/Af
|
|
Relative Temp Index, Elec
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
140
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.67
|
-
|
ASTM D 792
|
|
Filler Content
|
30
|
%
|
ASTM D 229
|
|
Mold Shrinkage on Tensile Bar, flow (2) (5)
|
0.1 - 0.3
|
%
|
SABIC Method
|
|
Mold Shrinkage on Tensile Bar, xflow (2) (5)
|
0.4 - 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate, 250°C/2.16 kgf
|
13
|
g/10 min
|
ASTM D 1238
|
|
Melt Flow Rate, 250°C/5.0 kgf
|
67
|
g/10 min
|
ASTM D 1238
|
|
Melt Flow Rate, 265°C/5.0 kgf
|
90
|
g/10 min
|
ASTM D 1238
|
|
Melt Flow Rate, 266°C/5.0 kgf
|
90
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.67
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.25
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.07
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 250°C/5.0 kg
|
40
|
cm3/10 min
|
ISO 1133
|
|
Melt Volume Rate, MVR at 265°C/5.0 kg
|
65
|
cm3/10 min
|
ISO 1133
|
|
Melt Viscosity, 260°C, 1500 sec-1
|
115
|
Pa-s
|
ISO 11443
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
ASTM D 257
|
|
Relative Permittivity, 1 MHz
|
3.5
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
ASTM D 150
|
|
Hot Wire Ignition {PLC)
|
0
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity, ROA
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, in oil, 0.8 mm
|
27
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 1.6 mm
|
23
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 3.2 mm
|
19
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity, 1 MHz
|
3.5
|
-
|
IEC 60250
|
|
Dissipation Factor, 50/60 Hz
|
0.001
|
-
|
IEC 60250
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
IEC 60250
|
|
Comparative Tracking Index
|
250
|
V
|
IEC 60112
|
|
Relative Permittivity, 50/60 Hz
|
3
|
-
|
IEC 60250
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
0.75
|
mm
|
UL 94
|
|
Glow Wire Flammability Index 960°C, passes at
|
3
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index (LOI)
|
34
|
%
|
ISO 4589
|