物理性能額定值 (公制)額定值 (英制)測試方法比重 |
1.14 g/cc
@Temperature 23.0 °C
|
1.14 g/cc
@Temperature 73.4 °F
|
ASTM D792 |
線性成型收縮率 |
0.0050 - 0.0070 cm/cm
@Temperature 23.0 °C
|
0.0050 - 0.0070 in/in
@Temperature 73.4 °F
|
ASTM D955 |
熔體流動速率 |
15 g/10 min
@Load 5.00 kg, Temperature 260 °C
|
15 g/10 min
@Load 11.0 lb, Temperature 500 °F
|
ASTM D1238 |
?
機械性能額定值 (公制)額定值 (英制)測試方法抗張強度(斷裂) | >= 50.0 MPa | >= 7250 psi | 50mm/min; ASTM D638 |
伸長率 (斷裂) | >= 60 % | >= 60 % | 50mm/min; ASTM D638 |
彎曲強度 | 82.0 MPa | 11900 psi | 2mm/min; ASTM D790 |
彎曲模量 | 2.20 GPa | 319 ksi | 2mm/min; ASTM D790 |
懸壁梁缺口沖擊強度 |
5.50 J/cm
@Thickness 3.20 mm, Temperature 23.0 °C
|
10.3 ft-lb/in
@Thickness 0.126 in, Temperature 73.4 °F
|
ASTM D256 |
懸壁梁無缺口沖擊強度 |
NB
@Thickness 3.20 mm, Temperature 23.0 °C
|
NB
@Thickness 0.126 in, Temperature 73.4 °F
|
ASTM D256 |
?
電氣性能額定值 (公制)額定值 (英制)測試方法體積電阻率 | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
表面電阻 | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
介電強度 | 30.0 kV/mm | 762 kV/in | 1.6mm; ASTM D149 |
?
熱性能額定值 (公制)額定值 (英制)測試方法載荷下熱變形溫度(0.46 MPa) |
124 °C
@Thickness 6.40 mm
|
255 °F
@Thickness 0.252 in
|
ASTM D648 |
載荷下熱變形溫度(1.8 MPa) |
106 °C
@Thickness 6.40 mm
|
223 °F
@Thickness 0.252 in
|
ASTM D648 |
可燃性(UL94) |
HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
HB
@Thickness 3.20 mm
|
HB
@Thickness 0.126 in
|
?
加工性能額定值 (公制)額定值 (英制)測試方法加工溫度 | <= 265 °C | <= 509 °F | |
料筒后部溫度 | 230 - 240 °C | 446 - 464 °F | Start Point: 240°C |
料筒中部溫度 | 230 - 250 °C | 446 - 482 °F | Start Point: 245°C |
料筒前部溫度 | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C |
加工(熔體)溫度 | 220 - 250 °C | 428 - 482 °F | Start Point: 245°C |
模具溫度 | 60.0 - 80.0 °C | 140 - 176 °F | Start Point: 70°C |
干燥溫度 |
100 - 110 °C
@Time 14400 - 21600 sec
|
212 - 230 °F
@Time 4.00 - 6.00 hour
|
Pre-dry |
背壓 | 0.300 - 1.00 MPa | 43.5 - 145 psi |