點擊圖片查看大圖| TEVOE PX7730 | Technical Data Sheet | |||
|
Product de |
||||
| Tevoe PX7730 is 30% glass-fibre reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyamide.This material has excellent mechanical properties and good surface effect.This material is specifically formulated forhigh strength and stiffmess applications where good impact resistance and excellent dimensional stability after molding are required.Its low viscosityand excellent flow properties make the material ideal for filling parts with thin-walled sections such as those encountered in the mobile electronics industry. | ||||
|
Tevoe PX7730 can be successfully plated, such as non conductive vacuum metallization, or coated with soft touch coating or UV topcoat coating. |
||||
| Filler / reinforcing material |
◆ 50% glass fiber reinforced materials |
|||
| Performance characteristics | ◆ Good dimensional stability. | ◆ Good impact resistance. | ||
| ◆ Fast production cycle. | ◆ Low warp. | |||
| ◆ Can be plating. | ◆ Good surface finish. | |||
| ◆ The moisture permeability is strong. | ◆ High strength. | |||
|
◆ High flow. |
||||
| Application | ◆ Thin wall components | ◆ Electronics / electrical applications. | ||
| ROHS compliance | ||||
| Processing method | injection molding | |||
| Product color | ◆ white | ◆ black | ||
| ◆ Natural color | ◆ Other | |||
| TEVOE PX7730 | Technical Data Sheet | |||
| Property | Test Condition | Unit | Standard | Value |
| Physical Properties | ||||
| Specific Gravity | - | g/cm3 | ISO 1183 | 1.56 |
| Water Absorption | 24hr，23℃ | % | ISO 62 | 0.38 |
| Mold Shrinkage | Trans | % | ISO 294 | 0.3 |
| Mechanical Properties | ||||
| Tensile Strength | 5mm/min | Mpa | ISO 527 | 245 |
| Elongation at Break | 5mm/min | % | ISO 527 | 2.3 |
| Tensile Modulus | 1mm/min,50mm span | Mpa | ISO 527 | 18600 |
| Flexural Modulus | 1mm/min,50mm span | Mpa | ISO178 | 16000 |
| Izod Notched Impact Strenth | 1/8in(3.2mm),Izod，23℃ | KJ/m2 | ISO178 | 15 |
| Thermal Properties | ||||
| Heat Deflection Temperature | 1.8MPa | ℃ | ISO75-2/A | 248 |
| Melting temperature | - | ℃ | ASTM D 34188 | 260 |
| vicat softening temperature | 50N;50℃/h | ℃ | ASTM D 648 | - |
| Burning behavior UL94(UL recognition) | 0.6mm,All colors | Class | UL-94 | HB |
| Other Propeties | ||||
| These property characteristics are taken fron the TEVOE plastics data bank and are base on the international catalogue | ||||
| of basic data for plastics according to ASTM. | ||||
| TEVOE PX7730 | Technical Data Sheet | |||
| Processing conditions for test specimens | ||||
| injection | Nominal Value Unit | |||
| Drying Temperature | 75 to 80℃ | |||
| Drying Time | 4 to 12 hr | |||
| Suggested Max moisture | 0.10% | |||
| Processing (Melt)Temp | 260 to 305℃ | |||
| Mole Temperature | 80 to 120℃ | |||
| Injection Pressure | 300 to 800 Mpa | |||
PPA TEVOE PX7730